Basic Info.
Model NO.
BH-4330
Technique
Phenolic Glass Fiber
Fiber Characteristics
E-Glass
Diameter of Filaments
Advanced Fibers
Fiber Appearance
Continous Fiber
Glass Composition
E-Glass
Shape
Chopped
Transport Package
Pallet
Specification
6mm
Trademark
Beihai
Origin
China
Production Capacity
10000/Month
Packaging & Delivery
Package Size
20.00cm * 30.00cm * 12.00cm
Package Gross Weight
1.000kg
Product Description
Phenolic Fiberglass Molding Plastics
This series of products are thermosetting molding plastics made of e-glass fiber and modified phenolic resin by soaking and baking. It is used for pressing heat-resistant, moisture-proof, mildew proof, high mechanical strength, good flame retardant insulating parts, but also according to the requirements of the parts, the fiber can be properly combined and arranged, with high tensile strength and bending strength, and suitable for wet conditions.
- Good mechanical properties: Our product offers excellent mechanical strength and durability, ensuring long-lasting performance.
- Electrical insulation: With superior electrical insulation properties, our product guarantees safety and reliability.
- Arc resistance and anti-static: Our product is specifically engineered to resist arcs and prevent static build-up, making it ideal for various applications.
- Good corrosion resistance: Our product is highly resistant to corrosion, including acid and alkali solutions, ensuring its longevity even in harsh environments.
- Lightweight: Designed to be lightweight, our product is easy to handle and transport.
- High product utilization: Our product maximizes its utility, providing efficient and effective results.
- Strong designability: With its versatile design, our product can be customized to meet specific requirements.
- Widely used: Our product finds extensive applications across various industries due to its exceptional properties.
| NO. | Test Items | Unit | Index | Test |
| 1 | Resin Content | % | Customized | 38.6 |
| 2 | Volatile Matter Content | % | 3.0-6.0 | 3.87 |
| 3 | Density | g/cm3 | 1.65-1.85 | 1.9 |
| 4 | Water Absorption | mg | ≤20 | 15.1 |
| 5 | Martin Temperature | ºC | ≥280 | 290 |
| 6 | Bending Strength | MPa | ≥160 | 300 |
| 7 | Impact Strength | KJ/m2 | ≥50 | 130 |
| 8 | Tensile Strength | MPa | ≥80 | 180 |
| 9 | Surface Resistivity | Ω | ≥10x10^11 | 10x10^11 |
| 10 | Volume Resistivity | Ω.m | ≥10x10^11 | 10x10^11 |
| 11 | Medium wearing factor (1MHZ) | - | ≤0.04 | 0.03 |
| 12 | Relative Permittivity (1MHZ) | - | ≥7 | 11 |
| 13 | Dielectric Strength | MV/m | ≥14.0 | 15 |
It is suitable for pressing mechanical components with high strength, electrical components with complex shape, radio parts, mechanical parts and electrical parts with high strength and commutator (commutator), etc. Its products also have good electrical performance, especially suitable for hot and humid areas.
It should be stored in a dry and ventilated room where the temperature does not exceed 30ºC.
Do not close to fire, heating and direct sunlight, erect stored on a special platform, horizontal stacking and heavy pressure are strictly prohibited.
Shelf life is two months from the date of production. After the storage period, the product can still be used after passing the inspection according to the product standards. Technical standard: JB/T5822-2015